Pseudomorphic Si/SiGe/Si body device with embedded SiGe source/drain

ABSTRACT

The invention relates to a semiconductor structure and method of manufacturing and more particularly to a CMOS device with at least one embedded SiGe layer in the source/drain region of the PFET, and at least one embedded SiGe layer in the channel region of the NFET. In one embodiment, the structure of the invention enhances the electron mobility in the NFET device, and further enhances the hole mobility in the PFET device. Additionally, by using the fabrication methods and hence achieving the final structure of the invention, it is also possible to construct a PFET and NFET each with embedded SiGe layers on the same substrate.

FIELD OF THE INVENTION

The invention relates generally to a semiconductor device and method of manufacturing, and more particularly to a semiconductor device and method of manufacturing an NFET and PFET device with stress components.

BACKGROUND DESCRIPTION

Mechanical stresses within a semiconductor device substrate can modulate device performance. That is, stresses within a semiconductor device are known to enhance semiconductor device characteristics. Thus, to improve the characteristics of a semiconductor device, tensile and/or compressive stresses are created in the channel of the NFETs and/or PFETs. But, it is well known that stress components affect the behaviors NFET and PFET devices differently.

In order to maximize the performance of both NFETs and PFETs within integrated circuit (IC) chips, the stress components should be engineered and applied differently for NFETs and PFETs. The stress components should be engineered and applied differently because the type of stress which is beneficial for the performance of an NFET is generally disadvantageous for the performance of the PFET. More particularly, when a device is in tension, the performance characteristics of the NFET is enhanced while the performance characteristics of the PFET is diminished.

To accommodate the different stress requirements, it is known to use different material combinations to apply tensile stress to NFETs and compressive stress to PFETs. In known processes for implementing stresses in FETs, distinct processes and/or materials are used to create the tensile or compressive stresses in the NFETs and PFETs, respectively. It is known, for example, to use a trench isolation structure for the NFET and PFET devices. According to this method, the isolation region for the NFET device contains a first isolation material which applies a first type of mechanical stress on the NFET device in a longitudinal direction and in a transverse direction. Further, a first isolation region and a second isolation region are provided for the PFET and each of the isolation regions of the PFET device applies a unique mechanical stress on the PFET device in the transverse direction.

Additional methods to provide strain for both NFET and PFET include the use of patterned, tensile or compressively strained silicon nitride layers for spacers or gate sidewalls, or for contact studs etch stop liners.

While these methods do provide structures that have tensile stresses being applied to the NFET device and compressive stresses being applied along the longitudinal direction of the PFET device, they require additional materials and/or more complex processing, and thus, result in higher cost. Also, the levels of induced stress with these methods tend to saturate and also become lower with technology scaling. Further, in current fabrication devices, a method and device including both NFET and PFET devices on the same substrate including an embedded SiGe layer in the gate region of the NFET, and an embedded SiGe layer in the PFET source/drain region are preferred during separate processes. These more recent methods provide strained channel NFET and PFET where the stresses increase with further gate length scaling and are not/little impacted by overall design ground rules scaling.

SUMMARY OF THE INVENTION

In a first aspect, the invention provides a method of fabricating a semiconductor device, including forming stress inducing layers under a first gate structure, protecting portions of the stress inducing layers under the first gate structure, protecting a second gate structure having a stress component associated therewith, etching unprotected areas of the stress inducing layers at sides of the first gate structure to form openings and a resulting stress component under the first gate structure, and filling the openings with material.

In a second aspect, the invention provides a semiconductor device structure including a substrate, first and second gate stacks disposed on the substrate, the first gate stack comprising at least one silicon layer, and a source/drain region adjacent to the first gate stack comprising a compressive inducing material to place the first gate stack in a compressive state, the second gate stack comprising a first silicon layer disposed on the substrate, and a tensile producing material disposed on the first silicon layer, and a second silicon layer disposed on the tensile producing material to induce a tensile stress component under the second gate stack.

A third aspect of the invention is a semiconductor device structure including a NFET device and a PFET device disposed on a substrate, the PFET device comprising a first gate stack, the NFET device comprising a second gate stack, wherein the first gate stack comprises at least one silicon layer and an adjacent source/drain region which comprises at least one silicon germanium layer to induce a compressive stress, and wherein the second gate stack comprises at least one silicon layer formed on a silicon germanium layer to induce a tensile stress.

BRIEF DESCRIPTION OF DRAWINGS

FIGS. 1 through 12 are representative of sectional schematic views of processing step(s) and structures in accordance with the invention (not to scale).

DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION

The invention relates to a semiconductor structure and method of manufacturing and more particularly to a CMOS device with at least one embedded SiGe layer in the source/drain region of the PFET, and at least one embedded SiGe layer in the channel region of the NFET. In one embodiment, the structure of the invention enhances the electron mobility in the NFET device, and further enhances the hole mobility in the PFET device. Additionally, by using the fabrication methods and hence achieving the final structure of the invention, it is possible to construct a compressively strained channel PFET and a tensile strained channel NFET on the same substrate, in same processing steps.

Referring to FIG. 1, an exemplary initial structure is shown. Specifically, the exemplary initial structure is comprised of an NFET region 10 and a PFET region 20 formed on a substrate 30. The substrate 30 can be any conventional substrate, for example, a buried oxide (BOX), or a conventional bulk type Si wafer or substrate.

Next, isolation areas 40 are formed to isolate the NFET region 10 and the PFET region 20. Any conventional isolation scheme can be used to isolate the NFET region 10 and the PFET region 20 on the substrate 30. The isolation methods include, for example, shallow trench isolation (STI), or any variation of the local isolation of silicon (LOCOS) method, as is well known and understood in the art. Thus, although the exemplary structure of FIGS. 1-12 uses shallow trench isolations (STIs) 40, any isolation structure is contemplated by the present invention.

In one illustrative technique to form the STIs 40, photoresist is formed on the substrate, patterned, and a trench is etched in a conventional manner. The trench may be filled with an oxide, for example, by chemical vapor deposition (CVD) techniques. The surface can then be planarized, such as by chemical mechanical polishing.

In an embodiment involving SOI substrates, the thickness of the layers 50 and 60 at the starting wafer level is approximately 500 Å, although other thicknesses are contemplated by the invention depending on the parameters and design characteristics of the final device. Regardless of the starting substrate (SOI or bulk silicon), NFET region 10 is recessed first by a silicon etch, while the PFET region 20 is protected from this etch, by a hard mask layer such as silicon nitride. The recess depth is approximately 300 Å, although other depths are contemplated by the invention depending on the parameters and design characteristics of the final device.

Following the recess of the NFET region 10, at least one pseudomorphic SiGe layer 70 is formed on the silicon or SOI layer 50 in the NFET region 10, followed by another silicon layer 75. In embodiments, the at least one pseudomorphic SiGe layer 70 is approximately 200 Å thick and the silicon layer 75 is approximately 100 Å thick; although other thicknesses are contemplated by the invention depending on the parameters and design characteristics of the final device.

The at least one pseudomorphic SiGe layer 70 is selectively formed in a conventional manner via epitaxial deposition, for example, using ultrahigh-vacuum chemical vapor deposition (UHVCVD), low pressure chemical vapor deposition (LPCVD), rapid thermal chemical vapor deposition (RTCVD), and low energy plasma enhanced chemical vapor deposition (LEPECVD). In embodiments, the amount of Ge in the SiGe layer 70 is approximately 20%; although other percentages are also contemplated by the invention, with the realization that higher concentrations will provide higher stress levels for the NFET device.

The exemplary embodiment of FIG. 1 further shows a silicon layer 75 formed on the at least one pseudomorphic SiGe layer 70. The deposition of the silicon layer 75 may be deposited in a conventional manner via any selective epitaxial silicon formation technique. The deposition of the silicon layer 75 can be performed in the same process step as the deposition of the pseudomorphic SiGe layer 70.

It should be understood that since Si has a smaller lattice constant (i.e., atom spacing) than Ge, when the Si layer 75 is grown on the at least one SiGe layer 70, the Si layer 75 will become strained in tension with further processing steps. As will be described further, the SiGe layer 70 will become strain relaxed and thus inducing tensile strain into the Si layer 75. A suitable thickness for the strained Si layer 75 is below the critical thickness, which is the maximum thickness that strained Si can grow on the at least one relaxed SiGe layer 70 without forming defects in the crystal structure (e.g., dislocations). By way of example but not limitation, the strained Si layer 75 is between approximately 100 Å and 200 Å thick, and more preferably approximately 100 Å. The use of the Si layer 75 and SiGe layer 70, e.g., stress inducing layers, may be used to place the NFET under a tensile stress as discussed in greater detail below.

FIG. 2 shows a polysilicon gate patterning process in accordance with the invention. In this process, a polysilicon gate 80 is patterned in both the NFET region 10 and the PFET region 20 by conventional patterning processes, which includes deposition of a silicon nitride layer acting as a hard mask and lithography and etching steps. By way of example, the lithography step entails applying a photoresist, exposing the photoresist to a pattern of radiation, and developing the pattern utilizing a conventional resist developer. Following the lithography step, a conventional etching process such as reactive-ion etching, plasma etching, ion beam etching or laser ablation may be employed in transferring the pattern to active areas of the NFET region 10 and PFET region 30 to form the polysilicon gates 80 in the NFET region 10 and PFET region 20. A SiN cap 90 will remain on the gate region. A reoxidation process is used to grow a thin oxide 104 on the gate sidewall as well as on the remaining exposed source/drain regions.

FIG. 3 represents the step of forming a sacrificial spacer 105 along the PFET gate sidewalls. In this processing, a sacrificial block material is deposited on the structure. In one embodiment, the sacrificial block material is a nitride material (e.g., Si₃N₄) and forms nitride layer 100, and is formed in a conventional manner, such as by chemical vapor deposition (CVD) using a silane source. Other techniques which may be suitable for forming a nitride layer include LPCVD and atmospheric pressure CVD (APCVD).

A photoresist mask 110 is then formed over the NFET region 10. Portions of the nitride layer 100 are subsequently etched in a conventional manner in the PFET region 20 to form sacrificial spacers 105. In embodiments, the spacers 105 are approximately 200 Å thick. Etching of the nitride layer 100 in the PFET region 20 can be performed for example, using anisotropic reactive ion etching (RIE).

As shown in exemplary FIG. 4, after formation of the sacrificial spacer 105 along the PFET gate sidewalls, the photoresist mask 110 (shown in FIG. 3) is removed from the NFET region 10, using conventional stripping methods known in the art. After the photoresist mask 110 is removed, the silicon or SOI layer 60 is partially etched using a conventional anisotropic silicon etching process. In embodiments, the silicon or SOI layer 60 is etched to form a trench of approximately 300 Å, although the etching depth can vary depending on the stress tailoring needs.

Referring to FIG. 5, an SiGe layer 120 is formed in the openings of the etched silicon or SOI layer 60 in the PFET region 20. In embodiments, the SiGe layer 120 is between approximately 300 Å and 500 Å thick, although other thicknesses can also be used depending on the depth of the etched area and of the intended overfill of the trench. The SiGe layer 120 can be selectively formed epitaxially in any conventional manner, for example, using UHVCVD, MBE, LPCVD, RTCVD, and LEPECVD, as noted above. The SiGe layer 120 will place the PFET device in a compressive state thus enhancing hole mobility.

Referring to FIG. 6, although not required, the exemplary embodiment may include a silicon layer 125 formed on the SiGe layer 120. The silicon layer 125 may be formed in any conventional manner to allow better silicide formation.

Referring still to FIG. 6, a liner 130 made of an oxide or nitride based material, for example SiO₂, is formed on the NFET region 10 and PFET region 20. In one embodiment, the liner is in the range of between approximately 20 Å and 50 Å thick.

A blocking mask material 140 is then formed on the PFET region 20 in order to perform a conventional etching process on the liner 130 in the NFET region 10. The purpose of the liner material is to protect the PFET areas during the selective epitaxial growth step that follows. The thickness of the liner 130 is not critical to the understanding of the invention and accordingly any thickness that provides a suitable protection of the PFET region 20 from the epitaxial growth on the NFET is contemplated.

Referring now to FIG. 7, the liner 130 and portions of the nitride layer 100 are removed from the NFET region 10 by anisotropic reactive ion etching (RIE) until the SiN cap 90 is reached, thereby forming sacrificial spacers 106 along the gate sidewalls in the NFET region 10.

Referring to FIG. 8, the blocking mask material 140 in the PFET region 20 is removed using conventional processes. In further processing steps, the pseudomorphic SiGe layer 70 and Si layer 75 which are not protected by the sacrificial spacers 106, are removed by anisotropic reactive ion etching (RIE). This leaves portions of the silicon or SOI layer 50 exposed. The SiGe layer 70 that was initially pseudomorphic to the Si substrate can now relax elastically by expanding laterally. As such, the Si layer 75 under the gate becomes strained in a tensile stress. The tensile stress of the Si layer 75 thus increases the electron mobility under the gate of the NFET region 10. Thus, the increased electron mobility under the gate of the NFET allows increased NFET performance at the same time with increased PFET performance.

Referring now to FIG. 9, a silicon raised source/drain 150 is selectively formed epitaxially onto exposed portions of the silicon or SOI layer 50 of the NFET region 10. As noted above, epitaxial formation of the silicon raised source/drain 150 can be performed by any conventional process, for example by UHVCVD, LPCVD, RTCVD, and LEPECVD. In one embodiment, the thickness of the silicon raised source/drain is between approximately 300 Å and 500 Å, depending on the specific device characteristics.

Referring to FIG. 10, liner 130, sacrificial spacers 105 and 106, and SiN caps 90 (all shown in FIG. 9) are removed by conventional dry or wet etching chemistry. For example, wet etch methods include use of a dilute hydrofluoric acid mixture optionally with glycerol, or hot phosphoric acid. Alternatively, dry etch methods include C₄F₈ chemistry, or plasma etch including CHF₃ and CF₄, depending on the material and desired etching depth, as is well known in the art.

FIGS. 11 and 12 show conventional processing steps performed to complete the device structure in accordance with an implementation of the invention. NFET and PFET extensions and halo implantation are performed, followed by with source/drain spacer formation 165 and 166, NFET and PFET source/drain implantations and final activation anneal. More specifically, the source/drain spacers 165 and 166 may be formed by, for example, deposition of a nitride material (e.g., Si₃N₄) deposited in a conventional manner, such as by chemical vapor deposition (CVD) using a silane source. Interconnect build-up using conventional wiring materials such as Cu can also be performed.

Extension implant of the NFET and PFET can be performed for example, by implantation of a dopant such as arsenic or boron (BF₂), respectively. In one embodiment, the implantation energy is about 1 KeV to 5 KeV, and dosage of the implantation may range from about 5e14 to 3e15 ions per cm². Halo implantation of the NFET and PFET can be performed for example, by implantation of a dopant such as arsenic or boron (BF₂), respectively. In one embodiment, the implantation energy is about 5 KeV to 50 KeV, and dosage of the implantation may range from about 1e13 to 3e14 ions per cm³.

Referring now to FIG. 12, a salicide process forms salicide areas 170. As is well known in the art, a self-aligned silicide process is performed wherein silicide contacts are formed only in those areas in which deposited metal (which after annealing becomes a metal component of the silicide) is in direct contact with silicon, whereby ohmic contacts to the source, drain, and gate are formed to produce salicide areas 170 in the NFET region 10 and PFET region 20. Following the salicide process, an interconnect build-up using conventional wiring materials such as Cu (not shown) can be performed in preparation for subsequent processing steps.

While the invention has been described in terms of embodiments, those skilled in the art will recognize that the invention can be practiced with modifications and in the spirit and scope of the appended claims. 

1. A method of fabricating a semiconductor device, comprising: forming stress inducing layers under a first gate structure; protecting portions of the stress inducing layers under the first gate structure; protecting a second gate structure having a stress component associated therewith; etching unprotected areas of the stress inducing layers at sides of the first gate structure to form openings and a resulting stress component under the first gate structure; and filling the openings with material.
 2. The method as claimed in claim 1, wherein the stress inducing layers comprise at least one SiGe layer and an upper Si layer.
 3. The method as claimed in claim 2, wherein the at least one SiGe layer comprises approximately 20% Ge.
 4. The method as claimed in claim 3, wherein the SiGe layer is approximately 200 Å thick.
 5. The method as claimed in claim 3, wherein the upper Si layer is approximately 100 Å thick.
 6. The method as claimed in claim 1, wherein the first gate structure is used to form an NFET device and the second gate structure is used to form a PFET device.
 7. The method as claimed in claim 1, further comprising forming a nitride protecting layer on the first gate structure to protect the first gate structure and portions of the stress inducing layers, and forming a liner to protect the second gate structure during the etching step and during selective epitaxial growth.
 8. The method as claimed in claim 1, wherein the step of etching unprotected areas of the stress inducing layers comprises etching an SiGe layer and an Si layer to an underlying SOI layer by reactive ion etching.
 9. The method as claimed in claim 1, wherein the stress component of the second gate structure is under a compressive stress, and is formed by etching an unprotected SOI layer and forming a SiGe layer in the etched portion, wherein the second gate is used for a PFET device.
 10. The method as claimed in claim 1, wherein the forming of the stress inducing layers includes forming an SiGe layer and an Si layer, and further comprising etching the SiGe layer and the Si layer to form a tensile stress under the first gate structure.
 11. The method as claimed in claim 1, wherein the stress inducing layers and the stress component are formed on a same substrate.
 12. The method as claimed in claim 1, wherein the stress inducing layers under the first gate structure are under a tensile stress, and the first gate is used for a NFET device.
 13. A semiconductor device structure, comprising: a substrate; first and second gate stacks disposed on the substrate; the first gate stack comprising at least one silicon layer, and a source/drain region adjacent to the first gate stack comprising a compressive inducing material to place the first gate stack in a compressive state; the second gate stack comprising a first silicon layer disposed on the substrate, and a tensile producing material disposed on the first silicon layer, and a second silicon layer disposed on the tensile producing material to induce a tensile stress component under the second gate stack.
 14. The device of claim 13, wherein the substrate comprises at least one of a silicon-on-insulator substrate and a buried oxide layer substrate.
 15. The device of claim 13, wherein the second gate stack further comprises a polysilicon gate disposed on the second silicon layer.
 16. The device of claim 13, wherein the compressive inducing material is SiGe disposed in openings of an underlying SOI layer adjacent to active areas of the first gate stack and the tensile producing material is SiGe forming part of the second gate stack.
 17. A semiconductor device structure, comprising: a NFET device and a PFET device disposed on a substrate; the PFET device comprising a first gate stack; the NFET device comprising a second gate stack; wherein the first gate stack comprises at least one silicon layer and an adjacent source/drain region which comprises at least one SiGe layer to induce a compressive stress; and wherein the second gate stack comprises at least one silicon layer formed on a SiGe layer to induce a tensile stress.
 18. The structure as claimed in claim 17, wherein the substrate comprises at least one of a silicon-on-insulator substrate, and a buried oxide layer substrate.
 19. The structure as claimed in claim 17, wherein the second gate stack further comprises silicon material on sides thereof to form source/drain regions.
 20. The structure as claimed in claim 17, wherein the source/drain region adjacent to the first gate stack further comprises a silicon layer disposed on first silicon germanium layer. 